The Effect of Composite Patches on the Failure of Adhesively-Bonded Joints Under Bending Moment

Abstract

In this study, it was aimed to compare mechanical behavior of double-strap joints with aluminum (AA2024-T3) or 16-ply laminate of carbon/epoxy composite (T300/934) patches of different orientation angles at their overlap area subjected to bending moment. For this purpose, AA2024-T3 aluminum was used as adherend, while the adhesive was a two-part paste (DP 460). Six different types of joint samples were subjected to bending moment. The effect of patch material on failure load and stress distribution was examined experimentally and numerically. In the numerical analysis, the composite patches were assumed to behave linearly elastic, while adherend and adhesive layers were assumed to be nonlinear. It was found that the data obtained from 3-D finite element analysis were coherent with experimental results. Meanwhile, experiments showed that fiber orientation angles of the patches markedly affected the failure load of joints, failure mode and stress distributions appeared in adhesive and composite.