INVESTIGATION OF THE EFFECTS OF SOME MODIFICATION PROCESS TO THE MECHANICAL PERFORMANCE AND DEFORMATION OF THE WOODWORK

Abstract

In this study, wood modification (thermo-processing and impregnation) and outdoor conditions of storage (natural aging) the effects on the mechanical performance of industrial woodwork was investigated. For this purpose, naturally grown in Turkey and the commercial value of high Scots pine (Pinus sylvestris L.) and chestnut (Castanea sativa Mill) wood was used. Experimental examples are specifically woodwork has been applied in actual size. Considering the previously conducted research literature only diagonal L-type samples used, not on the actual size samples of woodwork. In addition, there is no study that the combination of the heat-treatment and impregnation. This reveals the original values of this study. For preparing of samples is used the double tenon-mortise corner joint from constructions method and as glue polyurethane based Desmodur VTKA and Polyvinyl acetate based two-component D4. Diagonal woodwork test samples prepared by Thermo S class (185 degrees C temperature with a thermo-vapor process protections) applying. After application of the heat treatment, the test samples impregnated with a solution of 95 % natural pine cone resin and % 5 pine tannin by dip method (2 hours). Then, the untreated samples (control), only heat-treated samples and heat treatment + impregnated samples kept for 1 year with outdoor conditions (aging). At the end of the aging, the samples tested according to the principles stated in TS 2472 and TS 7251 EN 107 standard. As result, the performance of woodwork decreased after aging in untreated and heat treatment pieces, the other side after aging - heat treatment, impregnation materials increased the values. The deformation value of woodwork increased after aging most untreated materials, Heat treatment and heat treatment-impregnated reduced aging effectiveness.